The simultaneous codeposition of Pt and Ru on carbon materials was carried out potentiostatically at -0.5 V from H2PtCl6 and RuCl3 aqueous solutions in the presence of different organic additives: 1) ethylene glycol, 2) ethanol, 3) formic acid, 4) sodium citrate, 5) sodium tartrate and 6) Na2H2EDTA. The electrodeposition process was influenced thermodynamically and kinetically by the stabilizers. SEM and AFM analysis of the electrodes showed that both the particle size and the active surface area were notably affected by the presence of the stabilizing agents. The different behaviour of the stabilizing agents may be associated with the following effects: (1) the capability of the stabilizing agent to complex the metal ions, (2) the specific adsorption of organic molecules which inhibits particle growth, and (3) the reduction capability of the organic compounds. The electrodes prepared with different organic additives exhibit the following decreasing order of activities for methanol oxidation: citrate > tartrate > ethanol > Na2H2EDTA > ethylene glycol > formic acid > without stabilizer. This comportment can be related to differences in the active surface area, particle size and superficial structure of the metallic deposit.

La codeposición simultánea de Pt y Ru sobre materiales de carbono se llevó a cabo potenciostáticamente a -0,5 V a partir de soluciones acuosas de H2PtCl6 y RuCl3 en presencia de diferentes aditivos orgánicos: 1) etilenglicol, 2) etanol, 3) ácido fórmico, 4) citrato de sodio, 5) tartrato de sodio y 6) Na2H2EDTA. El proceso de electrodeposición fue influenciado termodinámica y cinéticamente por la presencia de los diferentes agentes estabilizantes. Los análisis SEM y AFM de los electrodos revelaron que el tamaño de las partículas y el área superficial activa de los catalizadores fueron notablemente afectados por la presencia de los agentes estabilizantes. Las diferencias en el comportamiento de los diferentes aditivos orgánicos en las soluciones de electrodeposición pueden ser asociadas con los siguientes efectos: 1) capacidad del estabilizante para acomplejar al ión metálico, 2) la adsorción específica de las moléculas orgánicas que inhiben el crecimiento de las partículas, y 3) la capacidad reductora de los compuestos orgánicos (sólo para los tres primeros aditivos). Los electrodos preparados con diferentes aditivos orgánicos presentan el siguiente orden decreciente de actividades catalíticas para la oxidación de metanol: citrato > tartrato > etanol > Na2H2EDTA > etilenglicol > ácido fórmico > sin estabilizante. Este comportamiento puede relacionarse con diferencias en el área superficial activa, tamaño de partícula y la estructura superficial del depósito metálico.

In this work the influence of the electrochemical oxidation of different carbon substrates, such as glassy carbon, graphite cloth, graphite felt, and carbon fiber paper, on the electrodeposition of bimetallic PtRu catalysts was studied. The oxidation of the different substrates prior to the catalyst deposition, leads to remarkable improvement of catalyst dispersion, reduction of particle size and higher specific surface area of the catalyst, when was compared than that electrodes with the unnoxidized substrates. All the electrodes were used to study the methanol oxidation in acid media.

Se estudió la influencia de la oxidación electroquímica de diferentes tipos de sustratos carbonosos, tales como carbono vítreo, telas de grafito, fieltros de grafito y papel de fibras de carbono y su empleo como soporte de catalizadores bimetálicos de PtRu preparados por electrodeposición. Se encontró que la oxidación de los diferentes sustratos en forma previa a la deposición de los catalizadores, llevaba a una dispersión más uniforme del catalizador, una considerable reducción del tamaño de partícula y un apreciable aumento del área superficial específica del catalizador, comparada con los electrodos obtenidos con el sustrato sin oxidar. Todos los electrodos preparados fueron usados para estudiar la oxidación de metanol en solución de H2SO4.